Rosa Blätter Grade 356.0 T6
Eigenschaften
Allgemeines
Eigenschaft | Wert | Bedingung |
---|---|---|
Dichte | 2,7 g/cm³ | T6 |
Mechanisch
Eigenschaft | Temperatur | Wert | Bedingung | Verwandte Standards | Form | Kommentar |
---|---|---|---|---|---|---|
Druckstreckgrenze | 172,0 - 186,0 MPa | T6 | ||||
Elastizitätsmodul | 72,0 GPa | T6 | ||||
72,4 GPa | T6 | |||||
Dehnung | -195 °C | 3,5 % | T6 | Sandguss, Dehnung in 50 mm | ||
-80 °C | 3,5 % | T6 | Sandguss, Dehnung in 50 mm | |||
-28 °C | 3,5 % | T6 | Sandguss, Dehnung in 50 mm | |||
3,0 % | T6 | Rosa Blätter, ASTM B108, ASTM B26, ASTM B618, ASTM B955 | Casting | A100 | ||
3,8 % | T6 | |||||
24 °C | 3,5 % | T6 | Sandguss, Dehnung in 50 mm | |||
100 °C | 4 % | T6 | Sandguss, Dehnung in 50 mm | |||
150 °C | 6 % | T6 | Sandguss, Dehnung in 50 mm | |||
205 °C | 18 % | T6 | Sandguss, Dehnung in 50 mm | |||
260 °C | 35 % | T6 | Sandguss, Dehnung in 50 mm | |||
315 °C | 60 % | T6 | Sandguss, Dehnung in 50 mm | |||
371 °C | 80 % | T6 | Sandguss, Dehnung in 50 mm | |||
Ermüdungsfestigkeit | 90 MPa | T6 | für 5x10⁸ Zyklen, R.R. Moore Type Test | |||
Härte, Brinell | 70,0 [-] | T6 | Rosa Blätter, ASTM B26, ASTM B618 | Casting | ||
80 [-] | T6 | 500 kg Belastung, 10 mm b | ||||
85,0 [-] | T6 | Rosa Blätter, ASTM B108, ASTM B955 | Casting | |||
Poisson-Zahl | 0,33 [-] | T6 | ||||
Schermodul | 27,2 GPa | T6 | ||||
Scherfestigkeit | 179 MPa | T6 | ||||
Zugfestigkeit | -195 °C | 275 MPa | T6 | Sandguss | ||
-80 °C | 240 MPa | T6 | Sandguss | |||
-28 °C | 227 MPa | T6 | Sandguss | |||
205,0 MPa | T6 | Rosa Blätter, ASTM B26, ASTM B618 | Casting | |||
220,0 MPa | T6 | |||||
230,0 MPa | T6 | Rosa Blätter, ASTM B108, ASTM B955 | Casting | |||
24 °C | 227 MPa | T6 | Sandguss | |||
100 °C | 220 MPa | T6 | Sandguss | |||
150 °C | 160 MPa | T6 | Sandguss | |||
205 °C | 83 MPa | T6 | Sandguss | |||
260 °C | 53 MPa | T6 | Sandguss | |||
315 °C | 28 MPa | T6 | Sandguss | |||
371 °C | 17 MPa | T6 | Sandguss | |||
Streckgrenze | -195 °C | 193 MPa | T6 | Sandguss, RP02 | ||
-80 °C | 172 MPa | T6 | Sandguss, RP02 | |||
-28 °C | 165 MPa | T6 | Sandguss, RP02 | |||
140,0 MPa | T6 | Rosa Blätter, ASTM B26, ASTM B618 | Casting | RP02 | ||
150,0 MPa | T6 | Rosa Blätter, ASTM B108, ASTM B955 | Casting | RP02 | ||
170,0 MPa | T6 | |||||
24 °C | 165 MPa | T6 | Sandguss, RP02 | |||
100 °C | 165 MPa | T6 | Sandguss, RP02 | |||
150 °C | 138 MPa | T6 | Sandguss, RP02 | |||
205 °C | 58 MPa | T6 | Sandguss, RP02 | |||
260 °C | 35 MPa | T6 | Sandguss, RP02 | |||
315 °C | 21 MPa | T6 | Sandguss, RP02 | |||
371 °C | 14 MPa | T6 | Sandguss, RP02 |
Thermisch
Eigenschaft | Temperatur | Wert | Bedingung | Verwandte Standards | Form | Kommentar |
---|---|---|---|---|---|---|
Wärmeausdehnungskoeffizient | 2.2e-05 1/K | T6 | ||||
Schmelzpunkt | 557,0 - 613,0 °C | T6 | Rosa Blätter, ASTM B108, ASTM B26, ASTM B618, ASTM B955 | Casting | ||
570,0 °C | T6 | |||||
Spezifische Wärmekapazität | 970,0 J/(kg·K) | T6 | ||||
100 °C | 960 J/(kg·K) | T6 | abgeleiteter Wert | |||
Wärmeleitfähigkeit | 150,0 W/(m·K) | T6 | ||||
25 °C | 150 W/(m·K) | T6 | abgeleiteter Wert |
Elektrik
Eigenschaft | Wert | Bedingung | Kommentar |
---|---|---|---|
Elektrische Leitfähigkeit | 23000000 S/m | T6 | Typische/abgeleitete Werte |
Elektrischer Widerstand | 4.42e-08 Ω·m | T6 | Typische Werte |
Spezifische elektrische Leitfähigkeit | 39,0 - 41,0 % InVeKoS | T6 | Typische Werte |
Chemische Eigenschaften
Eigenschaft | Wert | Bedingung | Verwandte Standards | Form |
---|---|---|---|---|
Aluminium | 90,1 - 93,3 % | T6 | ||
Kupfer | 0,25 % | T6 | Rosa Blätter, ASTM B108, ASTM B26, ASTM B618, ASTM B955 | Casting |
Eisen | 0,6 % | T6 | ||
0,60 % | T6 | Rosa Blätter, ASTM B108, ASTM B26, ASTM B618, ASTM B955 | Casting | |
Magnesium | 0,2 - 0,45 % | T6 | Rosa Blätter, ASTM B108, ASTM B26, ASTM B618, ASTM B955 | Casting |
Mangan | 0,35 % | T6 | Rosa Blätter, ASTM B108, ASTM B26, ASTM B618, ASTM B955 | Casting |
Andere | 0,15 % | T6 | ||
Silizium | 6,5 - 7,5 % | T6 | Rosa Blätter, ASTM B108, ASTM B26, ASTM B618, ASTM B955 | Casting |
Titan | 0,25 % | T6 | Rosa Blätter, ASTM B108, ASTM B26, ASTM B618, ASTM B955 | Casting |
Zink | 0,35 % | T6 | Rosa Blätter, ASTM B108, ASTM B26, ASTM B618, ASTM B955 | Casting |
Metall