AA-Standards Klasse 5456 O
Eigenschaften
Allgemeines
| Eigenschaft | Wert | Bedingung | Verwandte Standards |
|---|---|---|---|
| Dichte | 2,66 g/cm³ | O | AA-Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
Mechanisch
| Eigenschaft | Wert | Bedingung | Verwandte Standards | Kommentar |
|---|---|---|---|---|
| Elastizitätsmodul | 71,0 GPa | O | AA-Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 | |
| Plane-Strain-Bruchzähigkeit | 22,0 - 35,0 MPa·√m | Typisch für geschmiedetes Aluminium der Serie 5000 | ||
| Poisson-Zahl | 0,33 [-] | Typisch für geschmiedetes Aluminium der Serie 5000 | ||
| Schermodul | 26,0–26,5 GPa | Typisch für geschmiedetes Aluminium der Serie 5000 | ||
| Zugfestigkeit | 265,0 MPa | O | AA-Standards, ASTM B209 | |
| 270,0 MPa | O | AA-Standards, ASTM B209 | ||
| 275,0 MPa | O | AA-Standards, ASTM B209 | ||
| 285,0 - 360,0 MPa | O | AA-Standards, ASTM B209 | ||
| 285,0 - 365,0 MPa | O | AA-Standards, ASTM B210, ASTM B221, ASTM B241 | ||
| 290,0 - 365,0 MPa | O | AA-Standards, ASTM B209 | ||
| 310,0 MPa | O | AA-Standards |
Thermisch
| Eigenschaft | Temperatur | Wert | Bedingung | Verwandte Standards | Kommentar |
|---|---|---|---|---|---|
| Wärmeausdehnungskoeffizient | 20 °C | 2.3899999999999998e-05 1/K | O | AA-Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 | |
| 100 °C | 2.3899999999999998e-05 1/K | O | AA-Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 | ||
| Max. Betriebstemperatur | 150,0 °C | Typisch für geschmiedetes Aluminium der Serie 5000 | |||
| Schmelzpunkt | 570,0 - 640,0 °C | O | AA-Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 | ||
| Spezifische Wärmekapazität | 879,0 - 963,0 J/(kg·K) | Typisch für geschmiedetes Aluminium der Serie 5000 | |||
| Wärmeleitfähigkeit | 117,0 | O | AA-Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
Elektrik
| Eigenschaft | Wert | Bedingung | Verwandte Standards |
|---|---|---|---|
| Elektrische Leitfähigkeit | 17000000,0 S/m | O | AA-Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
| Elektrischer Widerstand | 5,88e-08 Ω·m | O | AA-Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
Chemische Eigenschaften
| Eigenschaft | Wert | Bedingung | Verwandte Standards |
|---|---|---|---|
| Chrom | 0,05 - 0,2 % | O | AA-Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
| Kupfer | 0,1 % | O | AA-Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
| Eisen | 0,40 % | O | AA-Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
| Magnesium | 4,7 - 5,5 % | O | AA-Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
| Mangan | 0,5 - 1,0 % | O | AA-Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
| Silizium | 0,25 % | O | AA-Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
| Titan | 0,2 % | O | AA-Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
| Zink | 0,25 % | O | AA-Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241 |
Technologische Eigenschaften
| Eigenschaft | ||
|---|---|---|
| Löten | Allgemein:Löten ist nicht bekannt oder entwickelt
| |
| Korrosionseigenschaften | Spannungsrisskorrosion:keine Schäden im Betrieb, begrenzte Schäden bei Labortests, allgemein:sehr gut, ohne Schutz in Industrie- oder Meerwasseratmosphäre
| |
| Allgemeine Bearbeitbarkeit | Allgemein:schlecht (O, H321, H116)
| |
| Arbeitbarkeit | allgemein (Zustand):akzeptabel (O), schlecht (H321, H116)
| |
Metall