AA 6061-O: Vielseitige Aluminiumlegierung für Fertigung & Korrosionsbeständigkeit
AA 6061 ist eine leicht verfügbare Legierung mit guter Oberflächenbeschaffenheit und Eignung zum Eloxieren. Einfache Schweißbarkeit und Lötbarkeit mit schöner Oberfläche. Beständig gegen Korrosion durch Seewasser und atmosphärische Bedingungen. Geeignet für Warmumformung.
Eigenschaften
Allgemein
| Eigenschaft | Wert | Zustand | Zugehörige Normen |
|---|---|---|---|
| Dichte | 2,7 g/cm³ | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
Mechanisch
| Eigenschaft | Wert | Zustand | Zugehörige Normen | Bemerkung |
|---|---|---|---|---|
| Biegewechselfestigkeit | 60,0 MPa | O | AA Standards | |
| Elastizitätsmodul | 69,0 GPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 | |
| Härte Brinell | 30,0 | O | AA Standards | |
| Ebenendehnungsbruchtötigkeit | 22,0 – 35,0 MPa·√m | Typisch für stranggepresste 6000er-Serie Aluminium | ||
| Poisson-Zahl | 0,33 | Typisch für stranggepresste 6000er-Serie Aluminium | ||
| Schubmodul | 26,0 – 26,5 GPa | Typisch für stranggepresste 6000er-Serie Aluminium | ||
| Zugfestigkeit | 125,0 MPa | O | AA Standards | |
| 150,0 MPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B483 | ||
| 155,0 MPa | O | AA Standards, ASTM B211, ASTM B316 |
Thermisch
| Eigenschaft | Temperatur | Wert | Zustand | Zugehörige Normen | Bemerkung |
|---|---|---|---|---|---|
| Wärmeausdehnungskoeffizient | 20 °C | 2,36e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 | |
| 100 °C | 2,36e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 | ||
| Schmelzpunkt | 580,0 – 650,0 °C | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 | ||
| Spezifische Wärmekapazität | 887,0 – 963,0 J/(kg·K) | Typisch für stranggepresste 6000er-Serie Aluminium | |||
| Wärmeleitfähigkeit | 155,0 – 180,0 W/(m·K) | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
Elektrisch
| Eigenschaft | Wert | Zustand | Zugehörige Normen |
|---|---|---|---|
| Elektrische Leitfähigkeit | 23.000.000 – 27.000.000 S/m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| Elektrischer Widerstand | 3,7e-08 – 4,35e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
Chemische Zusammensetzung
| Element | Gehalt | Zustand | Zugehörige Normen |
|---|---|---|---|
| Chrom | 0,04 – 0,35 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| Kupfer | 0,15 – 0,4 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| Eisen | 0,70 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| Magnesium | 0,8 – 1,2 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| Mangan | 0,15 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| Silizium | 0,4 – 0,8 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| Titan | 0,15 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| Zink | 0,25 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
Technologische Eigenschaften
| Eigenschaft | Bewertung |
|---|---|
| Löten | allgemein: möglich mit kommerziellen Verfahren und Methoden |
| Korrosionseigenschaften | Spannungsrisskorrosion: keine Schädigung im Betrieb und Labortests (O, T6, T651, T652, T6510, T6511), keine Schädigung im Betrieb, begrenzte Schädigung im Labortest (T4, T451, T4510, T4511), allgemein: gut, ohne Schutz in industrieller oder Seewasseratmosphäre |
| Allgemeine Zerspanbarkeit | Allgemein: mangelhaft (O), ausreichend (T4, T451, T4510, T4511, T6, T651, T652, T6510, T6511) |
| Umformbarkeit | allgemein (Zustand): gut (O), akzeptabel (T4, T451, T4510, T4511), mangelhaft (T6, T651, T652, T6510, T6511) |
EN 573-3 Güte AW-6056 T78 Aluminiumlegierung – Hochfeste aushärtbare AlMgSi
AW-6060 T64: Hochleistungs-, lebensmittelechte Aluminiumlegierung (EN 573-3 Güte)
Metall
- AA 6061 H13 Aluminiumlegierung – Hohe Festigkeit, korrosionsbeständig und leicht schweißbar
- AA Güte 5456 O Aluminiumstandard – Wichtige mechanische Eigenschaften der hochfesten AlMg-Legierung
- AA 5083-O Aluminiumlegierung – Hohe Festigkeit & Korrosionsbeständigkeit
- AA 6066 T6 Aluminiumlegierung – Eigenschaften & Spezifikationen nach AA Standards
- AA 6351 T6 – Aluminiumlegierung: Technische Standards & Eigenschaften
- AA 6061 T89 Legierung – Korrosionsbeständig, gut bearbeitbar, Premium-Qualität
- AA 6061 T94 Aluminiumlegierung – Hochleistungsgüte 6061 mit T94-Ausführung
- AA Standards Grade 5454 O – Umfassende Spezifikation der Aluminiumlegierung
- AA Standards 1060 O – Vollständige Materialspezifikationen & Normen
- AA 3004 O (Weichgeglüht): Umfassende Eigenschaften & Leistungsübersicht