SEW 470 Güte X8CrNi25-21 lösungsgeglüht (+AT)

-269,0 °C

205,5 GPa

-195,0 °C

205,5 GPa

-100,0 °C

206 GPa

20,0 °C

196 GPa

27,0 °C

143,7 GPa

100,0 °C

190 GPa

200,0 °C

182 GPa

300,0 °C

174 GPa

400,0 °C

166 GPa

500,0 °C

158 GPa

600,0 °C

150 GPa

700,0 °C

142 GPa

800,0 °C

134 GPa

900,0 °C

127 GPa

1000,0 °C

120 GPa

-269,0 °C

0,3 [-]

-195,0 °C

0,3 [-]

27,0 °C

0,29 [-]

-100,0 °C

1,49E-5 1/K

20,0 °C

1.61E-5 1/K

100,0 °C

1,67E-5 1/K

200,0 °C

1,55E-5 - 1,72E-5 1/K

300,0 °C

1,77E-5 1/K

400,0 °C

1,7E-5 - 1,81E-5 1/K

500,0 °C

1,84E-5 1/K

600,0 °C

1,75E-5 - 1,88E-5 1/K

700,0 °C

1,91E-5 1/K

800,0 °C

1,85E-5 - 1,94E-5 1/K

900,0 °C

1,97E-5 1/K

1000,0 °C

1.9E-5 - 2E-5 1/K

-100,0 °C

440 J/(kg·K)

20,0 °C

472 - 500 J/(kg·K)

100,0 °C

487 J/(kg·K)

200,0 °C

503 J/(kg·K)

300,0 °C

512 J/(kg·K)

400,0 °C

520 J/(kg·K)

500,0 °C

530 J/(kg·K)

600,0 °C

541 J/(kg·K)

700,0 °C

551 J/(kg·K)

800,0 °C

559 J/(kg·K)

900,0 °C

565 J/(kg·K)

1000,0 °C

571 J/(kg·K)

20,0 °C

11,9 - 15 W/(m·K)

100,0 °C

13,3 W/(m·K)

200,0 °C

15,1 W/(m·K)

300,0 °C

16,7 W/(m·K)

400,0 °C

18,3 W/(m·K)

500,0 °C

19 - 19,8 W/(m·K)

600,0 °C

21,3 W/(m·K)

700,0 °C

22,8 W/(m·K)

800,0 °C

24,3 W/(m·K)

900,0 °C

25,7 W/(m·K)

1000,0 °C

27,1 W/(m·K)

20,0 °C

3,3 mm²/s

100,0 °C

3,4 mm²/s

200,0 °C

3,7 mm²/s

300,0 °C

4,1 mm²/s

400,0 °C

4,3 mm²/s

500,0 °C

4,5 mm²/s

600,0 °C

4,7 mm²/s

700,0 °C

5 mm²/s

800,0 °C

5,4 mm²/s

900,0 °C

5,7 mm²/s

1000,0 °C

5,8 mm²/s